This is used to heat the steel parts to 482 to 621 deg c in an atmosphere of ammonia gas and dissociated ammonia. The case depth is depending upon the time kept in the inside chamber. Nitride forming elements are used for this method.
The advantage of the process is little distortion, the part can be tempered after being quenched. The quality of this depends on the precision of the furnace. The nitriding also could be done on solution nitriding using salt.

This is dual fuel furnace used for annealing or for doing any other processing. The burner used is of fully automatic fuel efficient. The furnace is fully lined with ceramic fixer for fuel efficiency and less heat leakage.

This is used to heat the carbon steel to appropriately 40 deg c above AC3 or AC1 for 1hr and slowly cooled 38 deg c 1hr usually furnace cooled. The furnace shall be offed while steel is still inside. This result is coarse pearlistic structure. Fully annealed steel is soft and ductile. This could be done is oil fired, electrical or L P G furnace . The furnace shall be automatically controlled and ceramin fiber insulated with suitable color and structure.

This is usually used for annealing application of heavy structure with moving bogie for easy accessibility for loading and unloading. This furnace is also durable as well as easy to install in various industries for different heating applications.

It is used for various heating applications where a round surface is more preferable. It can be availed from us at industry leading prices. This furnace is widely demanded in the global markets and are made using premium quality of materials.

In Carburizing furnace a process used harden steel with a carbon content between oil and 0.3 wt % c . In this process steel is introduced to a carbon rich environment and elevated temperature for a certain amount of time. Parts are heated at 927 deg c. Acetone, methanol and hydrogen are used for this process. Pack Carburizing and liquid Carburizing are also done using this furnace.

This is used for all paint baking application including powder coating. The size shall depend on the size of the job used for baking. The temperature varies from 80 to 180 deg c. This oven is also made with precision and attention to each and every intricate detail so that the best can be provided to the client.

This is specially used to treat aluminium before doing any shaping. The desired temperature is 350 to 400 deg C. This oven can easily melt the aluminum to the required level so that it can be used for several applications.

This is used in powder coating application. The temperature shall be of 180 deg C. This could be manufactured with fuel as electricity, LDO or LPG.

Industrial Driers are used for any drying application from the range of 40 deg celcious to 120 deg c. They are used in chemical plants, plastic granule drying, welding electrode heating, card board drying, paint drying, wood processing, clay drying etc.

This is a special purpose paint booth used in powder coating application. This is used in various industrial applications and can be customized as per the client requirements. This booth is also easy to install and is durable as well as corrosion resistant.

Thermocouples are the sensors used to receive the signal from the heating area in directly proportional to the rise of temperature. These are two dismillar metals joints to form one junction and produce milli volt directly proportional to the rise in temperature. We manufacture J,K,R,S,N and any other type.