We provide premium quality of ramming mass. We are specialized in manufacturing premix ramming mass. The ramming mass we offer comprises of binders such as boric acid that is mixed with pre-heated ramming mass. Our ramming mass better functionality and reduce the cost of production.
The chemical composition of our ramming mass is as follows:
- Silica (SiO2): above 99%
- Alumina (Al2O3): 0.04%
- Ferric Oxide (Fe2O3): 0.04%
- Titanium Dioxide (TiO2): 0.08%
- Manganese Oxide (MnO): Nil
- Calcium Oxide (CaO): Nil
- Magnesium Oxide (MgO): 0.11%
- Sodium Oxide (Na2O): 0.05%
- Potassium Oxide (K2O): Nil
- Loss in ignition - 0.08%
- Sintering Temp. - 1200oC
- Max. Service Temp. - 1700oC
Silica ramming mass is ideal for the following uses:
- SS Steel
- Plain carbon steels (M.S.)
- Alloy Steels
- Low manganese and low chromium steels
- All graded cast iron
- S.G. iron and malleable iron
- Alloy cast iron
Special features of ramming mass:
- High refractoriness to withhold operating temperature
- High corrosion resistance towards steel & slag
- High electrical resistivity to prevent short circuiting
- Suitable up to 1730ºC
- Consistent quality (purity 98.65%)
- Grain-sizes mixed according to capacity of the furnace
- Free of iron oxide (FeO)
- Minimum expansion & contraction at high temperature (treated)
- Moisture free and sea worthily packing
- Low down time for furnace lining
Our ramming mass is available in three different types such as:
- AK - 15 (ordinary grade): This is ideal for small capacity induction furnaces. It is suitable for capacity up to 1600ºC. It is weakly resistant to temperature.
- AK - 30 (snow white): The snow white model is suitable for higher capacity induction furnaces of up to 1730ºC. It exhibits better resistance to high temperature.
- AK - 45 (Pre-mixed--Our Specialized Product): This is a new innovative machine highly useful for material having zero moisture capacity. It is preheated and mixed with binder boric for effective results.