Hard Coat For Metal (Spray Coatings), PU Lacquer (Spray Coatings), Epoxy Lacquer (Spray Coatings), Lacquer For Silver (Spray Coatings)

Home

Profile

Products Range

Enquiry

:: Products Range ::

Electrophoretic Coatings For Jewellery	High Performance Electrophoretic Lacquers	Low Bake Electrophoretic Coatings
Black E.D. Coatings	Hard Coat For Metal (Spray Coatings)	PU Lacquer (Spray Coatings)
Epoxy Lacquer (Spray Coatings)	Lacquer For Silver (Spray Coatings)	Glass Coat (Spray Coatings)
Glass Bottle Coating (Spray Coatings)	Vaccum Metallizing Lacquer For Glass

Electrophoretic Lacquers And Coatings

Chemdale Coatings Private Limited (CCPL) are a renowned name in the manufacturing of of an extensive range of Electrophoretic Lacquers and Speciality Coatings. The wide range of our products consists of the following:

Electrophoretic Coatings For Jewellery

These are commonly also known as: Electrophoretic Coatings, E-Coat & Electro Coat

Products:

CEC-01: General purpose Electrophoretic Lacquer based on Acrylic resin. Product with an excellent outdoor durability for artificial jewellery.

S. No	Acrylic Electro-Coat		CEC - 01
1.	Specific Gravity (g/cm³)		1.01
2.	Non Volatile (%)		30±2
3.	Stoving (Metal Temperature)		140°-150°C for 20 mins
4.	Shelf Life		Six months
5.	Substrate		Metal
6.	Bath Preparation	Resin	30%

		D.M Water	70%
7.	Operating Solids		8-10%
8.	--Do--- Temperature		25±2°C
9	Deposition Time		20-60 Sec
10.	pH Value		4.2-5.2
11.	MEQ Value		40±2
12.	Conductivity		< 900
13.	Gloss		High
14.	Adhesion		100%
15.	Pencil Hardness		2 H
16	Acetone Double Rubs		100
17.	Perspiration Resistance		1 Cycle
18.	Salt spray		96 hrs
19.	QUV Test		500 hrs

Send Trade Enquiry

High Performance Electrophoretic Lacquers

Key Areas

CEC-02: High performance Electrophoretic Lacquers based on Polyurethane resin. Product with an excellent outdoor durability for Metal hardware based on Brass, Aluminum, Copper, Stainless Steel & Phosphated Mild steel.

S. No	High performance Electrophoretic Lacquers		CEC - 02
1.	Specific Gravity (g/cm³)		1.04
2.	Non Volatile (%)		50±2
3.	Stoving (Metal Temperature)		160±2°C for 20 min
4.	Shelf Life		Six Months
5.	Substrate		Metal
6.	Bath Preparation	Resin	20%
		D.M Water	80%
7.	Operating Solids		10 ± 1%
8.	--Do--- Temperature		25±2°C
9.	Deposition Time		30-60 Sec
10.	pH Value		4.2-5.2
11.	MEQ Value		40±2
12.	Conductivity		< 900
13.	Gloss		High
14.	Adhesion		100%
15.	Pencil Hardness		4-5 H
16.	Acetone Double Rubs		2000
17.	Perspiration Resistance		4 Cycle
18.	Salt spray		500hrs
19.	QUV Test		1000 hrs

Send Trade Enquiry

High Performance Electrophoretic Lacquers

Low Bake Electrophoretic Coatings

Key Areas

CEC-03: Low Bake Polyurethene Electrocoat base on Polyurethane resin. These coatings are for outdoor durability.

S. No	Low Bake Electrophoretic Coatings		CEC - 03
1.	Specific Gravity (g/cm³)		1.06
2.	Non Volatile (%)		50±2
3.	Stoving (Metal Temperature)		110±2°C for 30 min
4.	Shelf Life		6 Months
5.	Substrate		Metal
6.	Bath Preparation	Resin	20%

		D.M Water	80%
7.	Operating Solids		10 ± 1%
8.	--Do--- Temperature		25±2°C
9	Deposition Time		30-60 Sec
10.	pH Value		4.2-5.2
11.	MEQ Value		40±2
12.	Conductivity		< 900
13.	Gloss		High
14.	Adhesion		100%
15.	Pencil Hardness		3-4 H
16	Acetone Double Rub		500
17.	Perspiration Resistance		3 Cycle
18.	Salt spray		500 hrs
19.	QUV Test		1000 hrs

Send Trade Enquiry

Black E.D. Coatings

Key Areas

CEC-04: Black E.D coatings based on Hybrid Epoxy. Black E.D for automobile industry with one 1000 Hours of Salt spray.

S. No	Black E.D.		CEC - 04
1.	Specific Gravity (g/cm³)		1.10
2.	Non Volatile (%)		50±2
3.	Stoving (Metal Temperature)		160±2°C for 30 min
4.	Shelf Life		6 Months
5.	Substrate		Phosphated/Electro plated Metal
6.	Bath Preparation	Resin	20%

		D.M Water	80%
7.	Operating Solids		10 ± 1%
8.	--Do--- Temperature		25±2°C
9.	Deposition Time		30-60 Sec
10.	pH Value		4.2-5.2
11.	MEQ Value		40±2
12.	Conductivity		< 1400
13.	Gloss		High
14.	Adhesion		100%
15.	Pencil Hardness		3-4 H
16.	Acetone Double Rub		2000
17.	Perspiration Resistance		5 Cycle
18.	Salt spray		1000 hrs
19.	QUV Test		1000 hrs

Send Trade Enquiry

Hard Coat For Metal (Spray Coatings)

Product		2 - K Hybrid Clear Lacquer
Viscosity		45±5 Sec at 30°C
Density		0.96 ± 0.03
% Solid		40±2
Shelf Life		One Year
Substrates		Polished, Electroplated Metals
Application Characteristics
		Part By Weight / Volume
Mixing Ratio	Part A	1
	Part B	1
	Thinner	70%
Pot Life	15-20 Hrs
Spraying Viscosity	18±2 Sec at 30°C by Ford cup B-4
Drying OR	Flash off	20 min
	Baking	180°C for 1 min
	OR	160°C for 5 min
	OR	140° C for 10 min
Physical & Chemical Properties
Finish	Smooth & Uniform
Gloss	Excellent
Spreading Rate	55-60 Sq ft/Ltr
Weather Resistance	300 Hrs
Humidity Resistance	200 Hrs
Scratch Resistance	2.0 Kg
Pencil Hardness	3-4 H
Salt Spray – On Polished Metal	72 Hrs
Acetone Double Rub	3000

Send Trade Enquiry

PU Lacquer (Spray Coatings)

Product	2-K polyurethane clear lacquer – based on High performance Acrylic Polyol & Aliphatic Isocyanate.
Viscosity	55±5 Sec at 30°C
Density	0.98±0.03
% Solid	45±2
Shelf Life	Part-A One Year	Part-B Six Months
Substrates	Polished, Electroplated metals & Plastics
Application Characteristics
		Part By Weight / Volume
Mixing ratio	Part A	4
	Part B	1
	Thinner	30-40%
Pot Life	3-4 Hrs
Spraying Viscosity		18 ± 2 Sec at 30°C by Ford cup B -4
Drying OR	Surface	20 Min
	Tack free Drying	1 Hr
	Hard Drying	Overnight
	Forced Drying	60°C-80°C for 20-30 Min
Physical & Chemical Properties
Finish		Smooth & Uniform
Gloss		Excellent
Spreading Rate		55-60 Sq ft/Ltr
Weather Resistance		500 Hrs
Humidity Resistance		200 Hrs
Scratch Resistance		1.5 Kg
Pencil Hardness		3-4 H
Salt Spray		48 Hrs

Send Trade Enquiry

Epoxy Lacquer (Spray Coatings)

Product		2- K Epoxy Clear lacquer – Based on High performance Modified Epoxy – Polyamide
Viscosity		45± 5 Sec at 30°C
Density		0.96±0.03
% Solid		45±2
Shelf Life		One Year
Substrates		Polished, Electroplated metals and Engineering plastics
Application Characteristics
		Part By Weight / Volume
Mixing Ratio	Part A	4
	Part B	1
	Thinner	30-40%
Pot Life		3-4 Hrs
Spraying Viscosity		18±2 Sec at 30°C by Ford cup B-4
Drying OR	Surface	20 Min
	Tack free Drying	1 Hr
	Hard Drying	Overnight
	Forced Drying	60°C-80°C for 20-30 Min
Physical & Chemical Properties
Finish		Smooth & Uniform
Gloss		Excellent
Spreading Rate		55-60 Sq ft/Ltr
Weather Resistance		300 Hrs
Humidity Resistance		200 Hrs
Scratch Resistance		2.0 Kg
Pencil Hardness		3-4 H
Salt Spray		72 Hrs

Send Trade Enquiry

Lacquer For Silver (Spray Coatings)

Product		Thermo – Plastic Acrylic Clear Lacquer – based on High performance Modified Acrylic
Viscosity		120±5 sec at 30°C
Density		0.96±0.03
% Solid		30±2
Shelf Life		One Year
Substrates		Polished & Plated Metal & Plastic
Application Characteristics
Mixing Ratio	Lacquer	100 ml
	Thinner for Spray	130 ml
	Thinner for Dipping	200-250 ml
Spraying Viscosity	18±2 Sec at 30°C by Ford cup B-4
Drying OR	Surface Drying	10 min
	Tack free Drying	30 min
	Hard Drying	Overnight
	Forced Drying	60°C - 80°C for 20-30 min
Physical & Chemical Properties
Finish	Smooth & Uniform
Gloss	Excellent
Spreading Rate	60-70 Sq ft/ ltr
Weather Resistance	150 Hours
Humidity Resistance	100 Hours
Scratch Resistance	1.0 Kg
Pencil Hardness	2 H

Send Trade Enquiry

Glass Coat (Spray Coatings)

Product		3-K Epoxy Clear lacquer – Based on High Performance Epoxy Polyamide
Viscosity		45±5 Sec at 30°C
Density		0.96±0.03
% Solid		45±2
Shelf Life		One Year
Substrates		Glass
Application Characteristics
		Part By Weight / Volume
Mixing Ratio	Part A	79%
	Part B	20%
	Part C	1%
	Thinner	30-40%
Pot Life	3-4 Hours
Spraying Viscosity	18±2 Sec at 30°C by Ford cup B-4
Drying OR	Surface Drying	20 Min
	Tack Free Drying	1 Hr
	Hard Drying	Overnight
	Forced Drying	60°C-80°C for 20-30 Min
Physical & Chemical Properties
Finish	Smooth & Uniform
Gloss	Excellent
Spreading Rate	55-60 Sq ft/Ltr
Weather Resistance	300 Hrs
Humidity Resistance	200 Hrs
Scratch Resistance	2.0 Kg
Pencil Hardness	3-4 H
Water- Immersion Resistance	8 days

Send Trade Enquiry

Glass Bottle Coating (Spray Coatings)

Product	3-K Polyurethane Clear Glass Lacquer – Based on High performance Acrylic Polyol & Aliphatic Isocyanate.
Viscosity	55±5 Sec at 30°C
Density	0.98±0.03
% Solid	42±2
Shelf Life	Part A One Year	Part B Six Month	Part C One Year
Substrates	Glass
Application Characteristics
			Part By Weight / Volume
Mixing Ratio		Part A	79%
		Part B	20%
		Part C	1%
		Thinner	30-40%
Pot Life		3-4 Hours
Spraying Viscosity		18±2 Sec at 30°C by Ford cup B-4
Drying OR		Surface Drying	20 Min
		Tack Free Drying	1 Hr
		Hard Drying	Overnight
		Forced Drying	60°C-80°C for 20-30 Min
Physical & Chemical Properties
Finish		Smooth & Uniform
Gloss		Excellent
Spreading Rate		55-60 Sq ft/Ltr
Weather Resistance		500 Hrs
Humidity Resistance		200 Hrs
Scratch Resistance		1.5 Kg
Pencil Hardness		3-4 H
Water Immersion Resistance		72 hrs

Send Trade Enquiry

Vaccum Metallizing Lacquer For Glass

Metallizing Lacquer
Specific Gravity (g/cm³)		0.98
Non Volatile (%)		45±2
Stoving (Metal Temperature)		150±2°C for 30 min
Shelf Life		One Year
Substrate		Glass Metal
Gloss		High
Adhesion		100%
Spraying Viscosity	18±2 Sec at 30°C by Ford cup B-4
Drying	Surface Drying	20 Min
	Oven Drying	160°C for 30 Min
Physical & Chemical Properties
Finish	Smooth & Uniform
Gloss	Excellent
Spreading Rate	55-60 Sq ft/Ltr
Scratch Resistance	2.0 Kg
Pencil Hardness	3-4 H
Water- Immersion Resistance	8 days

Send Trade Enquiry


	Home \| Profile \| Products Range \| Contact Us \| Enquiry


	Copyright © Chemdale Coatings Private Limited, All Rights Reserved (Terms of Use) Developed by IndiaMART InterMESH Limited