This Wire Contains a high ferrite level in its austenitic structure, thus providing better weld ability together superior heat and corrosion resistance. As larger amounts of alloying elements are added. It becomes suitable for the welding joints where dilution from ferrite steel takes place.

Typical Application :

Its designed for the welding of dissimilar metals such as S.S and Carbon Steel & Low Alloy Steel

Weld Metal Analysis (Range) % :

C	Mn	Si		P	Cr	Mi
0.03max	1.3	0.65	0.030 max	0.030 max	23.0	12.3

Mechanical properties (Range) :

Tensile Strength MPa	Yield Stress MPa	Elongation (%) (L=4D)	Charpy V-notch impact strength
			Temp	Joules
590	NA	40	-20°C	50

Shielding Gas : CO₂

Flow Rate : 14-20 l/min

Recommended Current and Packing Data :

Size (mm)

Amps DC (+)

Voltage (V)

Weight (KGS)

0.8

130-190

20-24

1.0

130-190

21-30

1.2

180-220

22-35

1.6

250-290

Flux Cored Wires (Gfc 75)

Classification :

AWS/SFA 5.20: E71T-5

Charecteristics :

GFC-75 is a Basic Coated Flux Cored Wire with Excellent Characteristics and is suitable for steel with a Tensile Strength up to 600 N/MM2 Deposited Weld Metal. Shows Superior Crack resistance, excellent at low temperature of -20° to 30°

Typical Application :

Ship building, Machinery Structure, Bridge Construction, Selvage plant facilities.

Weld Metal Analysis (Range) % :

C	Mn	Si		P
0.04-0.10	0.90-1.50	0.30-0.65	0.030 max	0.030 max

Mechanical properties (Range) :

Tensile Strength MPa	Yield Stress MPa	Elongation (%) (L=4D)	Charpy V-notch impact strength
			Temp	Joules
510-650	500-600	22-30	-30°C	50-100

Shielding Gas : CO₂

Flow Rate : 14-20 l/min

Recommended Current and Packing Data :

Size (mm)	Amps DC (+)	Voltage (V)	Weight (Kgs)
0.8	100-140	20-24	15
1.0	100-140	21-30	15
1.2	120-300	22-35	15
1.6	200-400	23-37	15

Welding Position :

Flux Cored Wires (Gfc Ab-65)

FLUX CORED WIRES

GFC AB-65

Classification: DIN 8555: MSG 10-60C

Tubular wire with no slag for surfacing applications. Deposition has the same structure as chromium iron casting, resisting up to 1000⁰C with Ar-CO₂ shielding gas. Four overlapping runs. This wire can be welded also without shielding gas with the open arc welding procedure.

Typical Applications: Mullers, crushers, excavator shovels, ceramic moulds, etc

Shielding gas flow rate: Ar/ CO₂(EN439:M21)/NO GAS

16-20 I/min

Hardness as welded: HRc: 58-62

Current: DC+

Chemical properties of the deposited weld metal:

C	Si	P	S	Cr
3.50%	0.60%	<0.025%	<0.025%	30.00%

Diameter (MM)	Current (A)	Voltage (V)	Weight of spool
2.40	170-500	21-42	15 Kg

Flux Cored Wires (Gfc-308 L)

Classification :

AWS/SFA 5.22:E308LT-1

Charecteristics :

GFC-308L is fluxcored wire for all position welding to be used with CO₂ or Argon + CO₂ mixed shielding gases. This wire benefits from a fast freezing slag system

Typical Application :

Its designed for the welding of 18% Cr. 8% Ni Stainless Steel

Weld Metal Analysis (Range) % :

C	Mn	Si		P	Cr	Ni
0.03 Max	1.4	0.65	0.030 Max	0.030 Max	19.5	10.0

Mechanical properties (Range) :

Tensile Strength MPa	Yield Stress MPa	Elongation (%) (L=4D)	Charpy V-notch impact strength
			Temp	Joules
590	NA	45	-20°C	60

Shielding Gas : CO₂

Flow Rate : 14-20 l/min

Recommended Current and Packing Data :

Size (mm)	Amps DC (+)	Voltage (V)	Weight (Kgs)
0.8	130-190	20-24	15
1.0	130-190	21-30	15
1.2	180-220	22-35	15
1.6	250-290	23-37	15

Weld

Your enquiry has been sent
Close(X)

Processing...

Flux Cored Wires (Gfc-71)
Classification :

AWS/SFA 5.20: E71T-1 EN 758: T46 0 P C 1 H5

Charecteristics :

Tubular rutile flux-cored wire for single or multipass welding of carbon, carbon-manganese steels and similar tupes of steels, including fine grain ones, with CO2 shielding gas. The good weldability in all positions, excellent bead appearance, less spatter, a fast freezing and easy to remove slag

Typical Application :

Ship building, railways wagons, general fabrication welding, Pipe welding, bridges, automobile parts, tanks etc

Weld Metal Analysis (Range) % :

C

Mn

Si

P

0.04-0.10

0.90-1.50

0.30-0.65

0.030 max

0.030 max

Mechanical properties (Range) :

Tensile Strength MPa

Yield Stress MPa

Elongation (%) (L=4D)

Charpy V-notch impact strength

Temp

Joules

510-650

440-540

22-30

0°C

50-100

Shielding Gas : CO₂

Flow Rate : 14-20 l/min

Recommended Current and Packing Data :

Size (mm)

Amps DC (+)

Voltage (V)

Weight (KGS)

0.8

100-140

20-24

15

1.0

120-300

21-30

15

1.2

200-400

22-35

15

1.6

200-400

23-37

15

Welding Position :

Your enquiry has been sent
Close(X)

Processing...

Gee Limited

Flux Cored Wires Electrodes

High Tensile Low Alloy Steel Electrodes

Low Hydrogen Electrodes

Mild Steel Electrodes

Saw Wires & Fluxes Electrodes

Tig Filler Wires Electrodes

Tubular Electrodes

Other Products

Flux Cored Wires Electrodes

Flux Cored Wires (Gfc 309 L)

Flux Cored Wires (Gfc 75)

Flux Cored Wires (Gfc Ab-65)

Flux Cored Wires (Gfc-308 L)

Flux Cored Wires (Gfc-71)