POLYTONE AP 108 to AP 112 Series of ALKYL PHENOLIC ADHESIVE RESINS are heat reactive alkyl phenolic resins formulated for use in the manufacture of contact adhesives / cements based on polychloroprene or other elastomers. POLYTONE AP 108 (High Heat Resistance Resin)

Melting Point (Capillary)	70º C - 80º C
Viscosity of 60% solution in Toluene at 25º C by B 4 Ford Cup	35 - 65 sec
Methylol Content	8-13 %

Use of POLYTONE AP 108 imparts excellent green tack and cohesive strength in rubber based adhesives. POLYTONE AP 108 is useful for increasing the storage stability , heat resistance and non phasing of the adhesive. POLYTONE AP 108 is recommended for use in rubber based adhesives for shoe, furniture , building , automotive and many other industries. POLYTONE AP 109

Softening Point (Ball & Ring)	95º C - 110º C
Viscosity of 60% solution in Toluene at 25º C by B 4 Ford Cup	35 - 70 Sec
Methylol Content	10 - 14%

Use of POLYTONE AP 109 imparts good open time combined with excellent green tack and cohesive strength in rubber based adhesives. Use of POLYTONE AP 109 is also useful for increasing the storage stability and heat resistance of the adhesive.

POLYTONE AP 108 to AP 112 Series of ALKYL PHENOLIC ADHESIVE RESINS are heat reactive alkyl phenolic resins formulated for use in the manufacture of contact adhesives / cements based on polychloroprene or other elastomers.

POLYTONE AP 110
(High Melting Resin)

Softening Point (Ball & Ring)	110º C - 120º C
Viscosity of 60% solution in Toluene at 25º C by B 4 Ford Cup	35 - 75 Sec
Methylol Content	10 - 14%

Use of POLYTONE AP 110 imparts good open time combined with excellent green tack and cohesive strength in rubber based adhesives. Use of AP 110 is also useful for increasing the storage stability and heat resistance of the adhesive.

POLYTONE AP 111

Melting Point (Capillary)	70º C - 80º C
Methylol Content	14 - 18%

POLYTONE AP 111 is a heat reactive alkyl Phenolic resin formulated for use in  Neoprene rubber adhesives. Iimparts low initial viscosity and viscosity stability to adhesives of this type. AP 111 can also be used with the adhesive grades of chloroprene where good bond strength at room and elevated temperatures are required.
Up gradation of Neoprene and adhesive grades of Chloroprene rubber used in rubber based adhesives.

POLYTONE AP 112

POLYTONE AP 112 can also be used with the adhesive grades of chloroprene where good bond strength at room and elevated temperatures are required. Up gradation of Neoprene and adhesive grades of Chloroprene rubber used in rubber based adhesives. POLYTONE AP 112 is also used in Tung Oil, Long oil, based alkyl insulating varnishes, auto primer varnishes and wire enamels.

POLYTONE AP 113

Chemical Classification	POP Formaldehyde Resin(Resol)
Type	Heat Reactive/Vulcanising Resin
Physical Form	Broken Lumps
Colour	Pale Yellow
Melting Point (Capillary)	60º C - 70º C
Methylol Content	8 – 11 %

POLYTONE AP 113 is a heat reactive alkyl phenolic resin formulated for use cross linking of butyl rubber mainly used in the tyre industry. Mainly used in the tyre industry for curing of butyl rubber, also used in adhesives based on butyl rubber.

POLYTONE AP 120 an AP 121 are non heat reactive novolac thermoplastic alkyl phenolic resins.

POLYTONE AP 120

Colour	Pale Yellow/light Reddish Brown
Softening Point (Ball & Ring)	92º C - 103º C
Acid Value	67 mg KOH/ g resin (Max)

POLYTONE AP 120 is a non heat reactive thermoplastic alkyl phenolic resin designed to develop high tack levels in rubber compounds  which are used in tyre construction and mechanical goods.
POLYTONE AP 120 is used as tackfier in the manufacture of rubber goods such as tire/tyre industry.

POLYTONE AP 121

Softening Point (Ball & Ring)	90º C - 100º C
Acid Value	67 mg KOH/ g resin (Max)
Methylol Content	1.0% Max
Ash Content	0.1% Max
Acetone Insolubles	0.3% Max
Moisture Content	0.2% Max

POLYTONE AP 121 is a non heat reactive thermoplastic alkyl phenolic resin designed to develop high tack levels  in   rubber compounds  which are used in tyre construction and mechanical goods. This resin provides tack in elastomers that are usually difficult to tackify.

POLYTONE AP 121 is used as tackfier in the manufacture of rubber goods such as in tire industry and in the manufacture of mechanical goods.

POLYTONE AP 130 & AP 131 are non heat reactive thermoplastic alkyl phenolic resin designed to give a consistent performance as a reinforcing resin.

POLYTONE AP 130

Chemical Classification	PTBP Formaldehyde Resin(Novolac)
Type	Non Heat Reactive/Reinforcing Resin
Physical Form	Broken Lumps
Colour	Pale Yellow/light Reddish Brown
Softening Point (Ball & Ring)	90º C - 103º C
Acid Value	65 - 68 mg KOH/ g resin (Max)
Free Phenol	1.0% Max
Ash Content	0.1% Max

POLYTONE AP 130 is a non heat reactive thermoplastic alkyl phenolic resin designed to give a consistent performance as a reinforcing resin in synthetic and natural rubber based goods that require high hardness, excellent chip and abrasion resistance when cross linked with a methylene donor.
POLYTONE AP 130 is used as a reinforcing resin  in tire beads, shoe soles, apex strips and co-extruded window profiles.

POLYTONE AP 131

Chemical Classification	Phenol-POP Formaldehyde Resin( Novolac)
Type	Non Heat Reactive/Reinforcing Resin
Physical Form	Broken Lumps
Colour	Pale Yellow/light Reddish Brown
Softening Point (Ball & Ring)	90º C - 105º C
Acid Value	65 - 68 mg KOH/ g resin (Max)
Methylol Content	1.0% Max
Free Phenol	1.0% Max
Ash Content	0.5% Max

POLYTONE AP 131  is a non heat reactive thermoplastic phenol-alkyl phenol resin designed for use in synthetic and natural rubber based compounds in applications that require high hardness compounds that process easily.

POLYTONE K-93 to 97 are practically acidless, unsaponifiable Ketone Formaldehyde Resins which are very light in colour, have excellent light resistance and show but very slight tendency to solvent retention. Addition of these resins in general improves gloss, hardness, filling, adhesive strength and durability. Polytone Ketonic are available in pearl shaped granules.

Solubility:

POLYTONE KETONIC RESINS are soluble in alcohols(not in methanol), ketones, esters, glycol ether acetates, as well as in some aromatic & chlorinated hydrocarbons. They are however not soluble in water and in aliphatic hydrocarbons.

Application:

POLYTONE KETONIC RESINS are used in the manufacture of flexographic inks, gravure inks, lamination inks and ball point pen inks. These resins are highly effective in imparting gloss, adhesiveness in the inks and also in increasing the solid content in flexo & gravure inks. Use of these resins in ball point pen inks ensure that pastes and inks in writing instruments do not dry quickly yet set quickly after writing.

POLYTONE KETONIC RESINS are used in the manufacture of all types of nitrolacquers and are most suitable for paper lacquers. These resins are useful in the manufacture of PVC lacquers and for polishing lacquers and finishes for the surface treatment of wooden furniture and articles.POLYTONE KETONIC RESINS are used in heat seal coatings, primer and base coatings, gasoline resistant coatings, nail lacquers and in adhesives.

Properties

Melting Point Range (CAP)	85°C - 120°C
Viscosity Range(50% soln in spirit)	15sec – 25sec B4 FC
Hydroxyl Value Range	200 – 285

Chemical Classification	Rosin Modified Maleic Resin
Type	Oil Soluble
Physical Form	Broken Lumps
Colour (Gardner )	7 max
Softening Point (Ring & Ball)	115º C - 125º C
Viscosity of 60% solution in Xylene at 30º C by B 4 Ford Cup	35 - 45 Sec
Acid Value	20 mg KOH/ g resin (Max)

POLYTONE M-130 is used for improving the film hardness of nitrocellulose and chlorinated rubber paints.
Also used in sanding sealer and hammerton paints.

Chemical Classification	Rosin Modified Maleic Resin
Type	Oil Soluble
Physical Form	Broken Lumps
Colour	Yellow to light brown
Melting Point (Capillary)	125º C - 135º C
Viscosity of 50% solution in Toluene at 25º C by B 4 Ford Cup	30 - 40 Sec
Acid Value	20 mg KOH/ g resin (Max)

POLYTONE M-131 is used in Varnishes, Paints and Over Print Varnishes, N.C. Lacquers etc.

Chemical Classification	Rosin Modified Maleic Resin
Type	Spirit Soluble
Physical Form	Broken Lumps
Colour	Yellow to light brown
Melting Point (Capillary)	105º C - 120º C
Viscosity of 50% solution in Toluene at 25º C by B 4 Ford Cup	18 - 23 Sec
Acid Value	125 – 135 mg KOH/ g resin (Max)

POLYTONE M-135 is used in Spirit soluble varnishes, N.C. Lacquers, Road Marking Paints, Liquid Inks etc

Chemical Classification	Rosin Modified Penta Esterified Phenol Formaldehyde Resin
Physical Form	Broken Lumps
Colour	Yellowish-Brown
Melting Point (Capillary)	110º C - 120º C
Viscosity of 50% solution in Toluene at 30º C by B 4 Ford Cup	18 - 22 Sec
Acid Value	20 mg KOH/ g resin (Max)
MTO Tolerance of 50% solution in Toluene	1:6 Min

POLYTONE P-140 finds its use in paints, printing inks, insulating varnishes, oil varnishes, etc.

Chemical Classification	Rosin Modified Penta Esterified Phenol Formaldehyde Resin
Physical Form	Broken Lumps
Colour	Yellowish-Brown
Melting Point (Capillary)	135º C - 145º C
Viscosity of 50% solution in Toluene at 30º C by B 4 Ford Cup	28 - 36 Sec
Acid Value	20 mg KOH/ g resin (Max)
MTO Tolerance of 50% solution in Toluene	1:5 Min

POLYTONE P-141 finds its use in Liquid inks of scratch-proof & better solvent release properties.

POLYTONE PA 302 is a polymeric fatty acid based co-solvent grade non reactive polyamide resin in solid for suitable for flexographic and gravure printing inks.It has excellent adhesion to treated polyethylene and other plastics. Polytone PA 303 has good flexibility and very good solvent release properties.

Chemical Classification	Polymeric Fatty Acid Based Polyamide Resin
Type	Co-Solvent Grade
Physical Form	Broken Lumps
Colour	Bright light yellow
Softtening Point (Ball & Ring Method)	105° C - 115° C
Viscosity of 35% solution in 1:1 ratio of   Toluene:Butanol at 25°C by B 4 Ford Cup	65 -85 mPas
Acid Value	7 mg KOH/ g resin (Max)
Amine Value	7 mg KOH/ g resin (Max)

POLYTONE PA 303 is a polymeric fatty acid based co-solvent grade non reactive polyamide resin in solid form suitable for flexographic and gravure printing inks. This resin provides excellent resistance to grease and water, and good glossy sharp prints. It has excellent adhesion to treated polyethylene and other plastics. Polytone PA 303 has good flexibility and very good solvent release properties.

Chemical Classification	Polymeric Fatty Acid Based Polyamide Resin
Type	Co-Solvent Grade
Physical Form	Broken Lumps
Colour	Bright light yellow
Softtening Point (Ball & Ring Method)	105° C - 115° C
Viscosity of 35% solution in 1:1 ratio of   Toluene:Butanol at 25°C by B 4 Ford Cup	85 -120 mPas
Acid Value	7 mg KOH/ g resin (Max)
Amine Value	7 mg KOH/ g resin (Max)