S. G. Wires

Features:

* Steel wire with thin and uniform coating for continuous welding on unalloyed and structural steels.
* Excellent welding characteristics.
* Minimum spatter and stable arc under optimum welding condition.
* Excellent copper adherence.
* Close dimensional tolerance.
* Controlled cast and helix.

Chemical Composition Of Mig Wire

Values given are in percent maximum, unless shown otherwise

ELEMENT	REQUIREMENT
Carbon	0.06/0.15 %
Manganese	1.4/1.85 %
Silicon	0.80/1.15 %
Sulphur	0.03 % max
Phosphorous	0.025 % max

Diameter & Specification

Wire is available in the following diameter	0.80mm/ 1.0mm/ 1.2mm/ 1.6mm/
Specification as per	IS: 6419-1996 , AWS A5. 18-93 Class ER 70S-6.

Features:

*Copper coated continuous solid wire layer wounded on MS fermer for submerged arc welding along with agglomerated/fused fluxes.
*Thin and uniform copper coating ensures good conductivity for uniform feeding and welding.

Chemical Composition Of SAW Wire
Values given are in percent maximum, unless shown otherwise

ELEMENT	REQUIREMENT
Carbon	0.10
Manganese	0.30-0.62
Silicon	0.03
Sulphur	0.03
Phosphorous	0.03
Copper	0.15

Diameter & Specification

Wire is available in the following diameter	2.00, 2.50, 3.15, 4,00 (mm)
Specification as per	IS 7280, AWS 5.17 EL8, EM 12K, EH 14.

Packaging Wire shall be layer wound and suitably packed to guard against atmospheric influence, damage or deterioration during storage, transit and inspection.

Features:

* Purity is more than 99. 995% with low percentage of impurity.
* Remarkable adhesiveness.
* The surface of wire should be clean, smooth, and free from blister & roughness.

Chemical Composition Of Zinc Wire
Values given are in percent maximum, unless shown otherwise

ELEMENT	REQUIREMENT
Zn,Mn	99.95
Lead	0.025
Cadmiuim	0.02
Iron	0.01
Tin	0.001
Copper	0.002
Toatal Impurities	0.05

Diameter & Tolerance

	Wire is available in the following diameter	2.00, 2.50, 3.15, 4.00 (mm)
	The tolerance on diameter of the wire shall be:	+0, -0.05(mm)

PackagingZinc wire shall be supplied in coils of continuous lengths, closely coiled without any loose turns. The inner diameter of the coil shall be 300-600 mm. The coils shall be bound and fastened compactly at two places on the opposite ends of a diagonal of the coil using binding wires. Inside, the coil is packed by polythene and outside, by Hessian cloth.