Leading Manufacturer of SS 13-8 PH (UNS S13800 - AMS 5864), 2017 Aluminum and SS 17-4 PH UNS S17400 AMS 5643 DIN 1.4542 - Forged Block from Mumbai.

SS 13-8 PH (UNS S13800 - AMS 5864)
Interested in this product?
Request a Call Back

SS 13-8 PH (UNS S13800 - AMS 5864)

Rs 370 / KgGet Latest Price

Minimum Order Quantity: 50 Kg

Availability

Stainless Steel 13-8 is stocked by 25 North American distributors and produced by 17 large mills. Distributors will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required

This material is stocked primarily in Bar Products by 19 distributors but is also available to a lesser extent in Flat Rolled Products, Forging Products, Wire Products, and Casting Products.

Chemistry Data :

 

Aluminum

0.9 - 1.35

Carbon

0.05 max

Chromium

12.25 - 13.25

Iron

Balance

Manganese

0.2 max

Molybdenum

2 - 2.5

Nickel

7.5 - 8.5

Nitrogen

0.01 max

Phosphorus

0.01 max

Silicon

0.1 max

Sulphur

0.008 max

 



Additional Information:

  • Item Code: SS13-8PH_PipeTube

View Complete Details

Get Best Quote

2017 Aluminum
Interested in this product?
Request a Call Back

2017 Aluminum

Rs 276 / KgGet Latest Price

Minimum Order Quantity: 50 Kg

Introduction

Aluminium/aluminum and its alloys are essential materials in various industries such as aerospace, marine, construction, and automobile.

Aluminium/aluminum 2017 alloy is a heat treatable wrought alloy with intermediate strength. It is stronger than aluminium /aluminum 2011, but harder to machine. Workability is fair with ductility and formability better that aluminium / aluminum 2014. Arc and resistance weldability of this alloy are satisfactory while corrosion resistance is fair.

The following datasheet will provide more details about aluminium / aluminum 2017 alloy.

Chemical Composition

The following table shows the chemical composition of aluminium / aluminum 2017 alloy.

ElementContent (%)
Aluminum, Al91.5 - 95.5
Copper, Cu3.5 - 4.5
Iron, Fe0.7 max
Manganese, Mn0.4 - 1
Magnesium, Mg0.4 - 0.8
Silicon, Si0.2 - 0.8
Zinc, Zn0.25 max
Titanium, Ti0.15 max
Chromium, Cr0.1 max
Remainder (each)0.05 max
Remainder (total)0.15 max
Physical Properties

The physical properties of aluminium / aluminum 2017 alloy are outlined in the following table.

PropertiesMetricImperial
Density2.79 g/cm³0.101 lb/in³
Melting point513-641°C955 - 1185°F
Mechanical Properties

The mechanical properties of aluminium / aluminum 2017 alloy are tabulated below.

PropertiesMetricImperial
Tensile strength (annealed)179 MPa26000 psi
Yield strength (annealed)69 MPa10000 psi
Elongation (annealed)22%22%
Elastic modulus72 GPa10500 ksi
Shear strength (annealed)124 MPa18000 psi


Additional Information:

  • Item Code: AluminumAlloy_2017-RoundBar_Sheet_Pipe_Wire_ForgedBlock

View Complete Details

Get Best Quote

SS 17-4 PH UNS S17400 AMS 5643 DIN 1.4542 - Forged Block
Interested in this product?
Request a Call Back

SS 17-4 PH UNS S17400 AMS 5643 DIN 1.4542 - Forged Block

Rs 400 / KilogramGet Latest Price

Minimum Order Quantity: 50 Kilogram

BrandImported
Size1/2 inch, 3/4 inch, 1 inch
ApplicationGas Pipe, Structure Pipe, Hydraulic Pipe
Thread Size5 to 500mm
Green5600

Introduction

T630 is a 17-4 PH martensitic precipitation hardening stainless steel with a unique combination of high strength and good corrosive resistance. Supplied in either the H1075 (H580) aged condition with a tensile strength of 1000 Mpa minimum (HB 311 min.), or the H1150 (H620) double aged condition with a tensile strength of 930 Mpa minimum (HB 277 min.). It is characterised by high tensile strength and high yield strength obtained by solution annealing, followed by a single or double low temperature (precipitation) age hardening treatment. Coupled with a corosion resistance comparable to 304 austenitic stainless steel in many corrosive environments.630 in the H1075 (H580) aged condition can be re-aged if necessary at a higher temperature simply by heating at the required temperature for the required duration.630 in the H1075 (H580) And H1150 (H620) aged condition, can also be re-aged at a lower temperature by re-solution annealing, followed by age hardening at the required temperature for the required duration.It is used extensively by the Marine, Aerospace, Chemical, Petrochemical, Food Processing, Paper and general metalwork industries. Here it is employed for applications such as: Pump Shafts, Aircraft Fittings, Valve Stems, Hydraulic Fittings, Studs, Bushings, Screws, Fasteners, Couplings, Wear rings, Rollers and Food Handling Equipment etc.. Material Magnetic in all conditions.

Stainless steels are known as high-alloy steels. They contain about 4-30% of chromium. They are further divided into martensitic, austenitic, and ferritic steels. Another group of stainless steels are known as precipitation-hardened steels. They are a combination of austenitic and martensitic steels.

Grade 17-4 stainless steel is the most widely used steel of the precipitation hardening grade steels. It has high toughness, strength, and corrosion resistance..

Features:

  • Excellent durability
  • Fine finish
  • Sturdiness
COMPOSITION

Carbon 0.07 max. Manganese 1.00 max. Phosphorus 0.040 max. Sulfur 0.030 max. Silicon 1.00 max. Chromium 15.00 - 17.50 Nickel 3.00 - 5.00 Copper 3.00 - 5.00 Columbium plus Tantalum 0.15 - 0.45
Grinding and Polishing

440C in the hardened and tempered condition requires care with finish grinding and polishing to avoid overheating as this can lower the hardness and corrosion resistance.

Elevated Temperature Use

Excellent oxidation resistance up to 1100oF (540oC).Exposure to temperature range 600 – 900oF (290 – 480oC) long term may result in reduced toughness but this can sometimes be minimilized by using higher ageing temperatures. As a general guide for short term exposure at elevated temperatures the ageing temperature should be at least 50oF (28oC) above the working temperature.

Welding

May be welded satisfactorily by shielded fusion and resistance welded processes, however oxyacetylene welding is not recommended due to the posibility of carbon pick up Filler metal when required should be similar to the parent metal if strength is important otherwise standard austenitic stainless filler wire 308L may be satisfactory. Pre-heating is not generally required.Welding in the solution annealed condition may be carried out satisfactorily, however welding in the H1150 (H620) condition reduces the effects of high welding stresses. Following welding in the solution annealed condition, parts can be directly age hardened as required, however those in the H1150 (H620) condition should be re-solution annealed and then age hardened as required.

Applications
  • Nuclear reactor
  • Aircraft and gas turbines
  • Oil field
  • Chemical process components
  • Paper mill
Specifications

UNS S17400
ASTM A564
DIN 50602
AMS 5642
MIL-S-25043
Grade 630
WS 1.4542
ASME SA564
X5CrNiCuNb16-4
AFNOR Z6CNU1704



Additional Information:

  • Item Code: SS17_4_PH_UNSS17400_AMS5643_DIN14542_ForgedBlock
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai JNPT
  • Production Capacity: 500 MT per month
  • Delivery Time: 30 Day