Jay Enterprises

Grade	Medical Grade
Viscosity	Low Viscosity
Hardness	10 Shore A
Catalyst Type	Platinum
Brand	Siloczest
Grade Standard	Industrial Grade
Component	A+B Kit
Usage/Application	Mould Making
Cure Type	Platinum Cure
Packaging Size	1 Litre
Application	Keypads, Injection Moulding, Gaskets, Baby Products, Seals, Medical Parts
Color	Translucent

HLSR -6 SERIES is platinum based heat curing Liquid silicone rubber which is used for the casting and cloth embedding application. Its a food grade material. It cures at high temperature to a translucent high strength elastic rubber. Physical appearance : High Viscous Liquid Colour- Base : Translucent Mixing Ratio : 10 :1 ( By weight) 

Additional Information:

• Item Code: HLSR-635
• Production Capacity: 4000
• Delivery Time: quick

Packaging Size	1 Kg
Color	White
Catalyst Type	Condensation Cure
Brand	Siloczest
Grade Standard	Industrial Grade
Usage/Application	Mould Making
Thickness	20%

Use for Mold making applications like Fiber Casting, Pattern Making, Shoe Molding, Gypsum Board manufacturing, Cement & POP Molding, Candles Making , Statue/Idol Making, Soap making
Two-part silicon rubber: flowable liquid silicon and curing agent.Fast curing. Cures at room temperature within 8-12 hours.An exceptional fluidity and good operability, easy to demold.Good tensile and tear strength, low shrinkage.                                                                                                                                               MIX RATIO: 3-5% of catalyst, For instant setting use 5% . For medium fast setting use 3%.BY WEIGHT - Easy to use silicone rubber compound features a convenient mixing ratio by weight. Use weighing machine for proper measurement and to avoid mistakes.SHORE A HARDNESS: 20 A - This scale measures the hardness of flexible rubber molds. A 20 A hardness is in the Moderate soft range in molding grade.LOW VISCOSITY: You can easily mix and pour this rubber compound, creating one-block or two-block pieces or replicas with no vacuum degassing required.
PERFECT FOR ART AND INDUSTRIAL APPLICATIONS                                                                              Often used for molds to reproduce sculptures and other prototypes, casting plaster, POP,resins, and wax                                                                                        
FAST POT LIFE AND CURE TIMEIt takes no more than 1 hour for this compound to cure at room temperature if 5% catalyst used , with no noticeable shrinkage, and a 3-hour cure time if 3% catalyst used . For maximum results, store the products at room temperature

Additional Information:

• Production Capacity: 1000kg

Color	White
Catalyst Type	Condensation Cure
Brand	Siloczest
Grade Standard	Industrial Grade
Usage/Application	Mould Making

FEATURES

·         Two-part silicon rubber: flowable liquid silicon and curing agent.

·         Cures at room temperature within 3-4 hours.

·         An exceptional fluidity and good operability, easy to demold.

·         Good tensile and tear strength, low shrinkage.

·         High duplication times.

LSR silicon are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability .When mixed with 5％ curing agent, they can operated within 5 to 7 minutes, Complete rubber will be formed after 1-2 hours. With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts. This product is a white flowable liquid with a hardness of 1—30A° when cured. If customer make large products in multiple-piece molds, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise.

Curing agent and silicon proportion and their reaction： Added with 3％ of curing agent, silicon can still flow within 15 Min, mold can be released in 5-6 hours. Added with 5％ of curing agent, silicon can still flow within 5 minutes, mold can be released in 2-3 hours．

TECHNICAL GUIDELINES

1. Stir the base (Part A) well before use (except when depending on machine )
2. Shake the catalyst container (Part B) well before use.
3. This is a 100 Part A to 3-5 Part B mixing ratio by weight. Weigh the desire amount of base into a clean mixing container.
4. Weight the proper amount of catalyst into the container. Mix the base and catalyst together by stirring with a stick until a uniform color is obtained. Scrape the container walls and bottom well to insure a thorough mix.
5. Though it is often unnecessary to deair the material due to its low viscosity some may choose to do so. If so, place the container into a vacuum chamber and evacuate the entrapped air from the mixture using a vacuum pump capable of achieving 29 inches of mercury vacuum. The mixture will rise, crest and then collapse in the container. Interruption(bumping) of the vacuum may be necessary to prevent overflowing the container. Keep the mixture under full vacuum for 2-3 minutes.
6. Bleed air slowly into the vacuum chamber. When the chamber is at atmospheric equilibrium, remove the cover plate and take out the container.
7. Pour the deaired material slowly in a steady stream from one end of the mould so that the material flows evenly over the pattern. This should minimize entrapment of air bubbles under the flowing material. A”ready”mold may be poured firstly over the pattern, which will also help reduce the possibility of entrapping air on the pattern and in the cured rubber. A mold release agent may be applied on the pattern first to improve release.
8. Allow the rubber to cure for 4-8 hours at 25 Deg C before removing the cured rubber mold from the pattern. Heat acceleration not recommended with this product.
9. For best results, allow the mold to air cure an additional 24 hours before using it in production.

 

Additional Information:

• Item Code: SERV-2024-LSR
• Production Capacity: 10000
• Delivery Time: sameday delivery if you're located in Bangalore,outside the state,order to arrive within 2 to 3 days
• Packaging Details: Packaging is available in (1kg packing) (5kg Packing) (20kg Packing) (100kg Packing)

Packaging Size	5 Litre
Color	White
Catalyst Type	Condensation Cure
Brand	Siloczest
Grade Standard	Industrial Grade
Usage/Application	Mould Making
Material	Rilicone Rubber
Form	Liquid
Curing Time	2 - 3 hrs
Hardness(Shore A)	10 (Shore A)
Weight	5.25kg
Working Time Of Catalysed Mixture	2 - 4 min
Mixed Viscosity	3 - 5%
Temperature	150 degree selsious
Item Code	LSR-210
Is It Abrasion Resistance	Non Abrasion Resistance
Shelf Life	365 Days
I Deal In	New Only
Mixing Ratio	100:5
Heat Resistant	Yes
Country of Origin	Made in India

Silicone Rubber PERFECT FOR ART AND INDUSTRIAL APPLICATIONS Often used for molds to reproduce sculptures and other prototypes, casting plaster, POP,resins, and wax LOW VISCOSITY You can easily mix and pour this rubber compound, creating one-block or two-block pieces or replicas with no vacuum degassing required. 1 Appearance : white 2 Mixing proportion of curing agent : 3-5% 3 Operating time (@ 25 °C ) : 15-30 Min 4 Curing time (@ 25 °C ) : 4-6 hrs Hardness : 10 A° 6 Density : 1.08 g/cm3 7 Viscosity (@ 25 °C ) :7000±1000 cps 8 Tensile-strength : ≥26 kgf /cm2 9 Tear-strength : ≥16 kgf /cm 10 Elongation-break : ≥ 450 %

About this item

• Use for Mold making applications like Candle Making, Fiber Casting, Pattern Making, Shoe Molding, Gypsum Board manufacturing, Cement & POP Molding, Candles Making , Statue/Idol Making, Soap making
• Two-part silicon rubber: flowable liquid silicon and curing agent
• Good tensile and tear strength, low shrinkage
• Slow curing. Cures at room temperature within 2-4 hours
• An exceptional fluidity and good operability, easy to demold
• MIX RATIO: 5% of catalyst. More working time than fast curing. Bubbles free
• BY WEIGHT - Easy to use silicone rubber compound features a convenient mixing ratio by weight. Use weighing machine for proper measurement and to avoid mistakes.

• SHORE A HARDNESS: 10ᵒA - This scale measures the hardness of flexible rubber molds. A 10ᵒA hardness is in the very soft range in molding grade.
• POT LIFE AND CURE TIME: Pot life is 15 min and Curing time will 8 hrs. For maximum results, store the products at room temperature!

Packaging Size	1 Litre
Color	White
Catalyst Type	Condensation Cure
Thickness	20-25%
Brand	Siloczest
Quantity Per Pack	1
Grade Standard	Industrial Grade
Usage/Application	Mould Making
Curing Time	3days@24 c /15 min@150 c
Hardness(Shore A)	35

HLSR -6 SERIES is platinum based heat  curing  Liquid silicone rubber which is used for the casting and cloth embedding application. Its a food grade material. It cures at high temperature to a translucent high strength elastic rubber.

APPLICATION:

• Baby feeding bottle,
• Cloth Embedding,

1. Injection molding / Casting parts.